Creep-resistant magnesium alloys for automotive powertrain applications offer significant potential for vehicle weight reduction. In this study permanent mold casting, microstructure and creep behavior have been investigated for a series of ternary magnesium alloys (Mg-4Al-4X (X: Ca, Ce, La, Sr) wt%) and AXJ530 (Mg-5Al-3Ca-0.15Sr, wt%). A permanent mold was instrumented with twelve thermocouples and mold temperature was monitored during the casting process. Average mold temperature increased from 200°C to 400°C during a typical alloy casting series (fifteen to twenty castings). The cast microstructure for all alloys consists of primary α-Mg globular phase surrounded by eutectic structure which is composed of intermetallic(s) and α-Mg magnesium phases. The primary cell size of the AXJ530 increased from 18 to 24 μm with increasing mold temperature and a similar trend is expected for all alloys.

Solidification paths and phase stability have been investigated in the creep resistant Mg-Al-Ca based alloys for powertrain applications. The liquidus projection and isothermal sections of the Mg-Al-Ca ternary system were determined, including a ternary (Mg, Al)2Ca intermetallic compound. The solidification of the alloys in the α-Mg primary phase field involves L→α+(Mg, Al)2Ca eutectic reaction in a wide range of compositions and is terminated with invariant reactions that form Mg2Ca or Mg17Al12 phases. The (Mg, Al)2Ca is a high temperature phase and decomposes into Mg2Ca and Al2Ca phases between 773 and 673 K, but the transformation is kinetically quite slow at temperatures below 473 K. Based on this new knowledge, alloy modifications through quaternary elemental additions to improve the solid-solution strength and aging treatments to reinforce the α-Mg phase with precipitates have been demonstrated.

The effects of lubricant on lap shear strength of Spot Friction Welded (SFW) joints made of 6111-T4 alloys were studied. Taguchi L8 design of experiment methodology was used to determine the lubricant effects. The results showed that the lap shear strength increased by 9.9% when the lubricant was present at the top surface compared to that of the baseline (no lubricant) whereas the lap shear strength reduced by 10.2% and 10.9% when the lubricant was present in the middle and at the bottom surfaces compared to that of the baseline (no lubricant), respectively. The microstructure analysis showed a zigzag interface at the joint between the upper and the lower sheet metal for the baseline specimen, the specimens with the lubricant at the top and at the bottom. However, a straight line interface is exhibited at the joint between the upper and the lower sheet for the specimen with the lubricant in the middle. The weld nugget sizes of the lap shear tested specimens were measured.

Quantification of residual stresses is an important engineering problem impacting manufacturabilty and durability of metallic components. An area of particular concern is residual stresses that can develop during heat treatment of metallic components. Many heat treatments, especially in heat treatable cast aluminum alloys, involve a water-quenching step immediately after a solution-treatment cycle. This rapid water quench has the potential to induce high residual stresses in regions of the castings that experience large thermal gradients. These stresses may be partially relaxed during the aging portion of the heat treatment. The goal of this research was to develop a test sample and quench technique to quantify the stresses created by steep thermal gradients during rapid quenching of cast aluminum. The development and relaxation of residual stresses during the aging cycle was studied experimentally with the use of strain gauges.

Since muscles act to translate an electrical impulse from the central nervous system into motion, it is essential to have a suitable mathematical model for muscles and groups of muscles for a virtual soldier environment. This paper presents a methodology in which the muscle contraction is broken down into three distinct physiological processes: calcium release and re-absorption by the sarcoplasmic reticulum, the rate at which calcium binds and unbinds to troponin, and the generation of force due to cross-bridge cycling and the elasticity of the muscle fibers. These processes have been successfully modeled by Ding and Wexler as a system of coupled differential and algebraic equations. These equations give the calcium-time history and the force time history of the muscle. By varying the electrical stimulation rates, the muscles can produce forces of varying magnitude and duration over which the force can be maintained.

Microstructures and failure mechanisms of spot friction welds (SFW) in aluminum 5754 lap-shear specimens were investigated. In order to study the effect of tool geometry on the joint strength of spot friction welds, a concave tool and a flat tool were used. In order to understand the effect of tool penetration depth on the joint strength, spot friction welds were prepared with two different penetration depths for each tool. The results indicated that the concave tool produced slightly higher joint strength than the flat tool. The joint strength did not change for the two depths for the flat tool whereas the joint strength slightly increases as the penetration depth increases for the concave tool. The experimental results show that the failure mechanism is necking and shearing for the spot friction welds made by both tools. The failure was initiated and fractured through the upper sheet under the shoulder indentation near the crack tip.

We have developed new CAE tools in the concept design process based on First Order Analysis (FOA). Joints are often modeled by rotational spring elements. However, it is very difficult to obtain good accuracy. We think that one of the reasons is the influence of the nonlinear behavior due to local elastic buckling. Automotive body structures have the possibility of causing local buckling since they are constructed by thin walled cross sections. In this paper we focus on this behavior. First of all, we present the concept of joint analysis in FOA, using global-local analysis. After that, we research nonlinear behavior in order to construct an accurate joint reduced model. (1) The influence of local buckling is shown using uniform beams. (2) Stiffness decrease of joints due to a local buckling is shown. (3) The way of treating joint modeling considering nonlinear behavior is proposed.

A new method for crashworthiness optimization of vehicle structures is presented, where an early design exploration is done by the optimization of an equivalent mechanism approximating a vehicle structure. An equivalent mechanism (EM) is a network of rigid bodies connected by prismatic and revolute joints with special nonlinear springs. These springs are designed to mimic the force-displacement characteristics of thin-walled beams often found in the vehicle body structures. A computer software is implemented that allows the designer to quickly construct an equivalent mechanism model of a structure using a graphical user interface (GUI) to optimize the model for given objectives prior to final tuning using finite element (FE) models. A case study of a vehicle front substructure consisting of mid and lower rails is presented, which demonstrates that the new approach can obtain a better design with less computational resources than the direct optimization of a FE model.

The fundamental relationship between semi-solid processing and microstructure and their effect on the flow characteristics of semi-solid metals have been studied for several years. However, how the process related microstructure influences fatigue properties has not been given the same attention. This study examines the influence of process-related microstructure on the fatigue properties of semi-solid formed A357 alloys. High-solid-fraction (62% solid) and low-solid-fraction (31% and 36% solid) semi-solid formed A357 was tested in axial fatigue with a stress ratio (R) equal to -1. The high solid fraction (HSF) material had better fatigue properties than the low solid fraction (LSF) material. This is attributed to the fatigue crack initiation mechanisms, as related to the fatigue crack initiation features and the strengths of the materials.

The need for improved understanding of new magnesium alloys for the automotive industry continues to grow as the application for these lightweight alloys expands to more demanding environments, particularly in drivetrain components. Their use at elevated temperatures, such as in transmission cases, presents a challenge because magnesium alloys generally have lower creep resistance than aluminum alloys currently employed for such applications. In this study, a new die cast magnesium alloy, MEZ, containing rare earth (RE) elements and zinc as principal alloying constituents, was examined for its bolt-load retention (BLR) properties. Preloads varied from 14 to 28 kN and test temperatures ranged from 125 to 175°C. At all test temperatures and preloads, MEZ retained the greatest fraction of the initial imposed preload when compared to the magnesium alloys AZ91D, AE42, AM50, and the AM50+Ca series alloys.

Compositional and microstructural variations in a casting can often result in rather significant variations in the response to a given aging treatment, leading to location dependent mechanical properties. The objective of this study is to determine the effect of copper content and solidification rate on the aging behavior of a type 319 cast aluminum alloy. The nominal composition of the alloy is Al-7% Si-3.5% Cu-0.25% Mg, however, typical secondary 319 aluminum specifications allow copper levels to vary from 3-4%. Solidification rates throughout a casting can vary greatly due to, among other factors, differences in section size. To determine the effect of copper level and solidification rate on the aging response, aging curves were experimentally developed for this alloy. Three different copper levels (3, 3.5, 4%) and two solidification rates were used for this study. Aging temperatures ranged from 150-290°C with nine aging times at each temperature.

A failure prediction methodology that can predict sheet metal failure under arbitrary deformation histories including rotating principal stretch directions and bending/unbending with consideration of damage evolution is reviewed in this paper. An anisotropic Gurson yield criterion is adopted to characterize the effects of microvoids on the load carrying capacity of sheet metals where Hill’s quadratic anisotropic yield criterion is used to describe the matrix normal anisotropy and planar isotropy. The evolution of the void damage is based on the growth, nucleation and coalescence of microvoids. Mroz’s anisotropic hardening rule, which was proposed based on the cyclic plastic behavior of metals observed in experiments, is generalized to characterize the anisotropic hardening behavior due to loading/unloading with consideration of the evolution of void volume fraction. The effects of yield surface curvature are also included in the plasticity model.

This paper reviews the relationship of the anisotropy of plastic behavior of sheet metal to crystallographic textures and the effect of anisotropic plastic behavior on sheet forming processes Although the basis is crystallographic, the anisotropy of cubic metals can be approximated by a continuum yield criterion. Use of this criterion in analyses of sheet forming gives better results than the usual quadratic criterion.

The use of die cast magnesium for automobile transmission cases offers promise for reducing weight and improving fuel economy. However, the inferior creep resistance of magnesium alloys at high temperature is of concern since transmission cases are typically assembled and joined by pre-loaded bolts. The stress relaxation of the material could thus adversely impact the sealing of the joint. One means of assessing the structural integrity of magnesium transmission cases is modeling the bolted joint, the topic of this paper. The commercial finite element code, ABAQUS, was used to simulate a well characterized bolt joint sample. The geometry was simulated with axi-symmetric elements with the exact geometry of a M10 screw. Frictional contact between the male and female parts is modeled by using interface elements. Material creep is described by a time hardening power law whose parameters are fit to experimental creep test data.

This study is a life-cycle assessment (LCA) comparing two types of a powertrain structural component: one made of diecast primary aluminum and another hypothetical part made of semi-solid injection molded primary magnesium (Thixomolded®). The LCA provides an indication of the potential environmental burdens throughout the life-cycles of both parts, ranging from raw material acquisition to product end-of-life. Preliminary results show high sensitivity to selection of primary vs. secondary metals, and to the SF6 emission factor used in the model. Opportunities exist for reducing energy consumption using secondary instead of primary metals for both parts, although the use of such is influenced by market supply and demand

Federal standards that mandate improved fuel economy have resulted in the increased use of lightweight materials in automotive applications. However, the environmental burdens associated with a product extend well beyond the use phase. Life cycle assessment is the science of determining the environmental burdens associated with the entire life cycle of a given product from cradle-to-grave. This report documents the environmental burdens associated with every phase of the life cycle of two fuel tanks utilized in full-sized 1996 GM vans. These vans are manufactured in two configurations, one which utilizes a steel fuel tank, and the other a multi-layered plastic fuel tank consisting primarily of high density polyethylene (HDPE). This study was a collaborative effort between GM and the University of Michigan's National Pollution Prevention Center, which received funding from EPA's National Risk Management Research Laboratory.

Thermal distortions of friction disks caused by frictional heating modify pressure distribution on friction surfaces. Pressure distribution, in turn, determines distribution of generated frictional heat. These interdependencies create a complex thermoelastic system that, under some conditions, may become unstable and may lead to severe pressure concentrations with very high local temperature and stress. The phenomenon is responsible for many common thermal failure modes of friction elements and is known as frictionally excited thermoelastic instability (TEI). In the paper, one of the cases of TEI is investigated theoretically and experimentally. The study involves a two-disk structure with one fiction disk and one matching steel disk that have one friction interface. An unsteady heat conduction problem and an elastic contact problem are modeled as axisymmetric ones and are solved using the finite element method.

The effect of temperature and preload on the bolt load retention (BLR) behavior of AZ91D and AE42 magnesium die castings was investigated. The results were compared to those of 380 aluminum die castings. Test temperatures from 125 to 175°C and preloads from 7 to 28 kN were investigated. The loss of preload for AZ91D was more sensitive to temperature than that observed for AE42, especially at low preloads. In general, retained bolt-load was lowest in AZ91D. All test assemblies were preloaded at room temperature and load levels increased when the assemblies reached test temperature. The load-increase was dependent on the preload level, test temperature, alloy, and results from thermal expansion mismatch between the steel bolt and the magnesium alloy components, mitigated by the onset of primary creep. Thermal exposure (aging) of AZ91D at 150°C improved BLR behavior.

This paper describes a Life Cycle Assessment (LCA) done to evaluate the relative environmental performance of magnesium (Mg) and aluminum (Al) automatic transmission cases. Magnesium is considered a lighter weight substitute for aluminum in this application. Light weighting of vehicles increases fuel economy and is an important vehicle design metric. The objective of this LCA is to quantify energy and other environmental trade-offs associated with each alternative for material production, manufacturing, use, and end-of-life management stages. Key features of the inventory modeling and the data collection and analysis methods are included in this paper along with life cycle inventory profiles of aluminum and magnesium alternatives. The life cycle inventory (LCI) was interpreted using a set of environmental metrics and areas needing further research were identified. A qualitative cost assessment was done in conjunction with this LCA to highlight potential cost drivers.

New high-temperature Mg alloys are being considered to replace 380 Al in transmission cases, wherein bolt-load retention, and creep, is of prime concern. One of these alloys is die cast AE42, which has much better creep properties than does AZ91D but is still not as creep resistant as 380 Al. It is thus important to investigate bolt-load retention and creep of AE42 as an initial step in assessing its suitability as a material for transmission housings. To that end, the bolt-load retention behavior of die-cast AE42, AZ91D and 380 Al have been examined using standard M10 bolts specially instrumented with stable high-temperature strain gages. The bolt-load retention test pieces were die cast in geometries approximating the flange and boss regions in typical bolted joints. Bolt-load retention properties were examined as a function of time (at least 100 hours), temperature (150 and 175 °C) and initial bolt preload (14 to 34 kN).